硅铁按硅及其杂质含量，分为十六个牌号，其化学成分如下表：（根据GB2277-87)
| 牌号 | 化字成分％ | |||||||
| Si | Al | Ca | Mn | Cr | P | S | C | |
| 范固 | 不大于 | |||||||
| FeSi90All.5 | 87.0-95.0 | 1.5 | 0.5 | 0.4 | 0.2 | 0.04 | 0.02 | 0.2 |
| FeSi90Al3 | 87.0-95.0 | 3 | 0.5 | 0.4 | 0.2 | 0.04 | 0.02 | 0.2 |
| FeSi75All0.5-A | 74.0-80.0 | 0.5 | 1 | 0.4 | 0.3 | 0.035 | 0.02 | 0.1 |
| FeSi75All0.5-B | 72.0-80.0 | 0.5 | 1 | 0.5 | 0.5 | 0.04 | 0.02 | 0.2 |
| FeSi75All.0-A | 74.0-80.0 | 1 | 1 | 0.4 | 0.3 | 0.035 | 0.02 | 0.1 |
| FeSi75All.0-B | 72.0-80.0 | 1.5 | 1 | 0.5 | 0.5 | 0.04 | 0.02 | 0.2 |
| FeSi75All.5-A | 74.0-80.0 | 1.5 | 1 | 0.4 | 0.3 | 0.035 | 0.02 | 0.1 |
| FeSi75 AI1.5-B | 72.0-80.0 | 1.5 | 1 | 0.5 | 0.5 | 0.04 | 0.02 | 0.2 |
| FeSi75 AI12.0-A | 74.0-80.0 | 2 | 1 | 0.4 | 0.3 | 0.035 | 0.02 | 0.1 |
| FeSi75 AI12.0-B | 74.0-80.0 | 2 | 1 | 0.4 | 0.3 | 0.04 | 0.02 | 0.1 |
| FeSi75 A112.0-C | 72.0-80.0 | 2 | - | 0.5 | 0.5 | 0.04 | 0.02 | 0.2 |
| FeSi75-A | 74.0-80.0 | - | - | 0.4 | 0.3 | 0.035 | 0.02 | 0.1 |
| FeSi75-B | 74.0-80.0 | - | - | 0.4 | 0.3 | 0.04 | 0.02 | 0.1 |
| FeSi75-C | 72.0-80.0 | - | - | 0.5 | 0.5 | 0.04 | 0.02 | 0.2 |
| FeSi65 | 65.0-<72.0 | - | - | 0.6 | 0.5 | 0.04 | 0.02 | - |
| FeSi45 | 40.0-47.0 | - | - | 0.7 | 0.5 | 0.04 | 0.02 | - |
在炼钢工业中，利用硅铁粉在高温下烯烧能放出大量热这一特点，常作为钢锭帽发热剂使用以提高钢锭的质量和回收率。在其他方面的用途。磨细或雾化处理过的硅铁粉，在选矿工业中可作为悬浮相。在焊条制造业中可作为焊条的涂料。在生产钼铁中硅铁粉用于还原熟钼矿、铁鳞等氧化物。